7-1 Innovative Sn-Cu Eutectic based Solder with Higer Creep Resistance

Home>7-1 Innovative Sn-Cu Eutectic based Solder with Higer Creep Resistance

7-1 Innovative Sn-Cu Eutectic based Solder with Higer Creep Resistance

7-1 Innovative Sn-Cu Eutectic based Solder with Higer Creep Resistance


Compared with the mass of tin-based solders, Sn-Cu eutectic based solder, which contains no silver, has a superior performance-to-price ratio. It has been widely used in the domestic electronic manufacture in the processes of wave-soldering, dip soldering and manual welding.


However, low oxidation resistance of this alloy severely affected its application in high-reliability electronic products.

The main defect of this brazing filler metal is poor temperature structures, which severely affected its application in high-reliability electronic products. Low oxidation resistance is another disadvantage of this alloy, which increases the residues during the wave-soldering process and raises the cost as well.


As the problems mentioned above, we conducted thorough study. By the method of microalloy and addition of Co, Ni and P etc.,We successfully improved the properties of Sn-Cu solder, especially the high temperature stability at welding point and the oxidation resistance of brazing filler metal.


The study shows that, addition of Co and Ni can change the morphology of the compounds on the interface of solder/Copper substrate. Figure 1(a) and (b) show the significant differences in compound's morphology at the interface of the traditional Sn-Cu/Cu and SC-Co-Ni-(p)/Cu. It can be found that traces of Co and Ni have the ability to transform the coarse scalloped compound at the interface into close-grained laminar structure. Although the layer of this product could be thicker in as-welded condition, because of the dense and flat interface, stress concentration is unlikely to happen when the welding point suffers external stresses. Therefore, compared with the scalloped compound, the mechanical properties of the joint has been improved, especially the shock resistance and anti-shake performance.


Latest study shows that, this laminar compound has a prominent advantage that its high temperature stability is much better than scalloped compound's. In the high temperature aging test, its growth rate is much lower than that of scalloped compound.


More importantly, it can be found that close-grained laminar compounds effectively inhibit the formation of Cu3Sn at the side of Cu substrate. Figure 2 shows the microstructure of the interface after heating at 150℃ for 24h,t can be concluded that Cu3Sn has already generated in the scalloped compound, while there is little Cu3Sn in the close-grained laminar compound. As we all know, the fomation of Cu3Sn is due to the different diffusion velocity of Sn and Cu in the interface, as well as the appearance of Kenkidall cavity, which is the main cause of degeneration of mechanical properties, especially the Creep Resistance. At the scalloped interface, Sn and Cu diffuse easily through the scalloped Cu6Sn5, so Cu3Sn can be easily obtained; while there is no such diffusion channel in the laminar interface, so the speed of the formation of Cu3Sn is reduced greatly.


Figure 3 shows the results of creep resistance test at the joint of Sn-0.7Cu and SC-Co-Ni-P respectively after high temperature aging at 150℃ for 24h. T is observed that the creep resistant at the joint of this solder alloy is more than doubled.


At the same time, the wettability of the alloy has also been improved. Figure 4 shows the wettability test results of the two kinds of alloy on the surface of copper. The alloy is of low cost because it contains no Pb and Ag, which are either inhibited or expensive, and its welding technological performances are close to Sn-0.7Cu. It can be applied to the field of packaging of various electronic products, especially those which serve at high temperature for a long period of time.

   This alloy has already applied for the state invention patent, and the patent application number is 2009100705088.

Proprietary Product



Contact us

Zhongya(tianjin) Electronic Solder Technology Co.Ltd
Address:Xingfa Road,Balitai Industrial Zone,Jinnan District,Tianjin,PR China
Tel:86-022-83981122
Fax:86-022-83981133
Email:zhongyasolder@zhongyasolder.cn
在线中文字幕亚洲 | 欧一美一性一交一乱一性一 | 欧美老妇一区二区 | 国产精品久久久久久久久久免费看 | 亚洲日韩在线观看不卡 | 国产又粗又硬又猛的毛片视频 | 91精品国产综合久久久久久久 | 最近中文字幕免费MV第一季歌词 | 夜夜夜夜午夜一级AA | 中文字幕 - 蛋播视频 | 国产成人无码a区视频网站 99人妻无码精品系列蜜桃 | 国産精品久久久久久久 | 美女航空一级毛片在线播放 | 91视频国产精品porny | 国产成人综合久久久久久 | 女人被狂躁60分钟视频 | 欧美成人在线视频观看 | 无码人妻一区二区三区一 | 精品无人妻一区二区三区免费蜜桃 | 国产白嫩白嫩wwwwwww裸体 | 欧美疯狂婬乱AAAA片免费 | 人妻少妇精品无码专区久久 | 成人午夜A片一区二区 | EEUSS影院www免费手机 | 色妻熟女乱色一区二区三区 | 久久精品国产亚洲AV麻豆 | 免费AA在线观看 | X9X9X9搡BBBB搡BBB jzzjzzjzz亚洲成熟少妇 | 91人妻无码精品一区二区 | 2025精品偷拍视频 | 99精品丰满人妻无码视频 | 国产成人无码A片V99麻豆 | 91福利所导航第一页 | 亚洲无码免费蜜桃一区91 | 寡妇高潮一级毛片免费看亚y洲二区 | 精品人妻久久一区二区三区久久精 | 四川一级丰满女老板毛 | 国产精品偷乱一区二区三区 | 中文字幕在线视频观看 | 国产乱国产乱300精品 | 午夜无码一区啊啊啊 |